Molten aluminium electromagnetic iron remover is necessary, manufacturers in industries such as industrial aluminum smelting, aluminum alloy smelting, إلخ. will encounter a problem, هذا هو, they need to charge aluminum ingots or recycled aluminum scraps into melting furnaces for high-temperature smelting and melting.
When aluminum products are heated at high temperatures, under the environment, it melts into molten aluminum, but in the smelting process, iron impurity elements are unavoidable in scrap aluminum.
If iron impurities are not quickly removed, سيؤثر بالتأكيد على جودة منتجات الألمنيوم, especially the elements in aluminum alloys.
The ingredients cause the product to be unqualified, or not suitable for sand casting or finished product, which significantly reduces the mechanical properties of the final product.
Molten aluminum electromagnetic iron remover is an effective tool for iron removal in the melting process.
Structure of molten aluminum electromagnetic iron remover
There is a heat dissipation layer on the surface of the high temperature resistant molten aluminum electromagnet iron remover.
يمكن تدوير طبقة تبديد الحرارة بواسطة الرياح لإزالة درجة حرارة سطح مزيل الحديد الكهرومغناطيسي.
طبقة تبديد الحرارة مغطاة بمادة عازلة للحرارة العالية للعزل الحراري.
الغلاف الخارجي للمواد العازلة مصنوع من الفولاذ غير الموصل (الفولاذ المقاوم للصدأ).
Working principle of molten aluminum electromagnetic iron remover
يمكن وضع القشرة في فرن بدرجة حرارة عالية تصل إلى 800 درجة مئوية, moving back and forth in molten aluminum.
ينتج مزيل الحديد الكهرومغناطيسي ذو درجة الحرارة العالية مجالًا مغناطيسيًا قويًا في الأسفل.
يمكن للمجال المغناطيسي اختراق الطبقة الواقية من الفولاذ المقاوم للصدأ, طبقة عازلة للحرارة, وطبقة خافضة للحرارة.
Attract and remove iron scraps and ferromagnetic impurities in the molten aluminum of melting furnace, ويمكن أن تولد مجالًا مغناطيسيًا عند تنشيطها, وإزالة الأجزاء الحديدية الممتصة عند انقطاع التيار الكهربائي.
The price and technical data can be sent as we get your inquiry.
The completed solution and one-stop service!
How do you remove iron impurities from molten aluminum?
Iron impurities can be removed from volumes of molten aluminum by applying electromagnetic iron remover.
The molten aluminum electromagnetic iron remover is an effective tool for iron removal in the melting process.
يمكن وضع القشرة في فرن بدرجة حرارة عالية تصل إلى 800 درجة مئوية, moving back and forth in molten aluminum.
ينتج مزيل الحديد الكهرومغناطيسي ذو درجة الحرارة العالية مجالًا مغناطيسيًا قويًا في الأسفل.
يمكن للمجال المغناطيسي اختراق الطبقة الواقية من الفولاذ المقاوم للصدأ, طبقة عازلة للحرارة, وطبقة خافضة للحرارة.
Attract and remove iron scraps and ferromagnetic impurities in the molten aluminum of the melting furnace, ويمكن أن تولد مجالًا مغناطيسيًا عند تنشيطها, and remove the attracted iron parts when the power is off.
Iron in aluminum, it is the most harmful impurities
Aluminum is one of the most versatile materials used in foundry practice; ومع ذلك, iron is one of the most troublesome impurities in aluminum cast materials.
During the solidification of aluminum alloys, الحديد يعزز تشكيل المراحل المتوسطة, مما قد يؤدي إلى الإضرار بخصائص المنتج النهائي.
In secondary aluminum industries, من الممكن دائمًا تلوث الحديد الناتج عن كميات كبيرة من خردة الحديد.
Iron is considered one of the most harmful impurities in aluminum.
This is especially noticeable in the manufacture of cast aluminum alloys for casting in a metal mold and a sand mold.
Iron along with aluminum and other alloying elements, مثل المنغنيز, نحاس, يشكل المغنيسيوم والسيليكون مرحلة وسيطة من الحديد, مما يقلل بشكل كبير من الخواص الميكانيكية للمنتج النهائي.
The main pollution of iron in aluminum, it occurs during the melting of aluminum scrap, الذي يخلط بالحديد.
علاوة على ذلك, Aluminum scrap may itself contain a high concentration of iron. انه ينتمي, على سبيل المثال, to waste aluminum casting alloys under pressure.
To minimize the problem of pollution of aluminum scrap iron, aluminum industry employs rigorous scrap sorting before loading it into a melting furnace.
وهذا ينطوي على الفرز اليدوي, الفرز المغناطيسي والفرز الكهرومغناطيسي لفرز كثافة جزيئات الخردة المسحوقة.
Iron particles in liquid and solid aluminum
In the conventional solidification of aluminum-silicon casting alloys, the first aluminum phase usually begins to harden.
تبقى المكونات الأخرى للسبيكة سائلة وتتراكم في المناطق الواقعة بين حبيبات المرحلة الأولية.
يؤدي التلوث بالحديد إلى حدوث تغيير في تسلسل مراحل التصلب: أولاً, the iron-containing intermediate phase appears, and only then does crystallization occur alumina grains.
When these particles are formed before aluminum, يمكن أن تنمو بحرية وبالتالي تنمو في بلورات خشنة محاطة بمرحلة سائلة.
The situation of iron removal from aluminum
أصبحت الجودة المعدنية ذات أهمية متزايدة بالنسبة للعجلات المعدنية, and for aluminum casting producers, due to the material cost of aluminum alloys, المشكلة أكثر خطورة: the cost of primary aluminum will erode the revenue of large-scale orders, and the low-quality secondary aluminum will reduce productivity for foundries or die casting plants.
بخاصة, the trace elements of iron-containing materials in recycled aluminum can make the final material brittle and limit its use in high-value automotive or aerospace applications.
Iron is generally harmful to aluminum alloys, مما يؤدي إلى تكوين مركبات بين المعادن.
ويتركز الحديد في عملية إعادة التدوير المستمرة, which makes the recycled aluminum brittle and limits its use in high-end applications such as airplanes.
Existing methods of removing iron from molten aluminum in the recycling process are either expensive or inefficient.